7150铝合金热变形行为及微观组织

采用Gleeble热模拟机进行热压缩实验,研究7150铝合金在变形温度为300~450℃、应变速率为0.01~10s-1条件下的变形行为,采用Zener-Hollomon参数法构建合金高温塑性变形本构方程,并对变形后的微观组织进行分析。研究表明:7150铝合金的流变应力随应变速率增大而增大,随变形温度增大而降低。该合金热压缩变形的流变应力行为可用双曲正弦形式的本构方程描述,其参数A为4.161×1014s-1,α为0.01956 MPa-1,n为5.14336,热变形激活能Q为229.7531k J/mol。随着温度升高和应变速率降低,动态再结晶逐渐取代动态回复成为合金的主要软化机制。     

表面处理对17-4PH不锈钢抗固体粒子冲蚀性能的影响

为对比研究表面处理对17-4PH不锈钢抗固体粒子冲蚀性能的影响,在17-4PH不锈钢表面进行了多弧离子镀陶瓷/金属多层膜制备、激光表面合金化(LSA)处理和超音速火焰喷涂(HVOF)硬质合金层处理,利用划痕仪、自组装的不锈钢抗固体粒子冲蚀(SPE)装置、多冲疲劳试验机对上述三种表面处理试样的小攻角和大攻角SPE失效行为和机理进行了研究。结果表明,微切削是17-4PH不锈钢及其表面改性试样小攻角下固体粒子冲蚀破坏的主要失效机制,多冲型疲劳破坏是17-4PH不锈钢及其表面改性试样大攻角下固体粒子冲蚀的主要失效机制。HVOF WC-17Co涂层可显著提高17-4PH不锈钢30°小攻角和90°大攻角下SPE抗力。激光表面合金化层能够改善17-4PH不锈钢抗30°小攻角和90°大攻角下SPE性能,但SPE性能改善效果弱于HVOF喷涂涂层。TiAl N/Ti多层膜不能显著提高17-4PH不锈钢抗30°小攻角和90°大攻角的SPE性能。     

熔体混熔制备Si相增强Al-8wt．％Si合金

采用熔体混熔方法结合挤压铸造制备了Al—8wt．％Si合金。利用SEM、DSC、TEM和力学性能测试等分析手段研究了合金的组织及性能。结果显示,通过将高温的A1-30％Si合金熔体和低温的工业纯铝金属液混和,凝固形成的亚共晶成份Al.08wt．％Si合金中含有3％左右的细小初生si相。与传统熔体变质处理后制备Al．8wt．％Si合金的相比,经初生Si相增强的Al—Si合金拉伸强度达到185MPa,抗弯强度达到437MPa,分别提高15％和19％,同时延伸率增加近1倍达到6．7％。     

TC11钛合金钨极氩弧焊工艺试验研究

针对TC11钛合金材料进行了自动钨极氩孤焊接工艺试验,获得了成形良好的焊缝,焊接质量符合航空Ⅰ级焊缝标准.采用金相试验方法和力学性能试验对不同焊接填充材料下的显微组织和性能进行对比.结果表明,采用TC11同质焊丝可获得与母材抗拉强度相当的焊接接头,略高于采用TA2纯钛焊丝的接头,但采用TA2焊丝时的集中塑性接近母材.     

7075铝合金在不同温度盐水环境中的腐蚀疲劳行为

基于飞机结构材料7075铝合金在沿海地区服役时海水飞溅及曝晒导致的高温腐蚀疲劳损伤问题,研究了7075铝合金在35,55,75℃下3.5%NaCl溶液环境中的腐蚀疲劳寿命,并使用扫描电子显微镜(SEM)观察断口形貌,探讨了温度对腐蚀疲劳裂纹萌生扩展的影响机理。结果表明:同一应力水平下,温度越高,腐蚀疲劳寿命越短,300MPa时35,55,75℃下的中值寿命分别为33 001,30 931,15 346次循环。腐蚀损伤和疲劳损伤存在竞争关系,应力水平较高时,腐蚀较轻,试样寿命主要受应力水平影响,疲劳源多从铝合金基体与包铝层结合处萌生;应力水平较低时,腐蚀较严重,疲劳寿命随温度升高明显下降,疲劳源多从腐蚀坑处萌生。断口形貌显示高温环境主要通过加速腐蚀坑的形成来影响疲劳源的萌生,深坑状腐蚀坑应力集中严重,对疲劳性能伤害大。     

Dynamic analysis of C/C composite finger seal

A seal device as an important component of aeroengines has decisive influence on per- formance, reliability, and working life of aeroengines. With the development of aeroengines, demands on the performance characteristics of seal devices are made strictly. Finger seal as a novel kind of sealing device, recently attracts more and more attentions in academic circles and engineer- ing fields at home and abroad. Research on finger seals has been extensively developed, especially on leakage and wear performances under dynamic conditions. However, it is a pity that the work on finger seals has been limited with a single approach that is improving the performance by structural optimization; in addition, the technology of dynamic analysis on finger seals is weak. Aiming at the problems mentioned above, a distributed mass equivalent dynamic model of finger seals considering the coupling effect of overlaid laminates is established in the present paper, the dynamic perfor- mance of 2.5 dimension C/C composite finger seal is analyzed with the model, and then the effects of fiber bundle density and fiber bundle preparation direction on finger seal＇s dynamic performance are discussed, as well as compared with those of Co-based alloy finger seal. The current work is about dynamic analysis of finger seals and application of C/C composite in this paper may have much academic significance and many engineering values for improving research level of finger seal dynamics and exploring feasibility of C/C composite being used for finger seals.     

二次时效对微合金化的Al-Cu-Li 微观组织及力学性能的影响

通过常规力学性能、扫描电镜、透射电镜等测试分析方法研究了T8I6二次时效制度对Mg、Ag和Zn复合微合金化的Al-3.48Cu-1.44Li合金微观组织和力学性能的影响.结果表明,与单级时效相比,二次时效合金强度提高,而塑性略降;合金强度随第三级时效时间的延长进一步提高.最优的合金其抗拉强度(UTS)、屈服强度(YS)和延伸率分别为613.7、564.9 MPa和6.8％.合金的强化相主要为T1相,另有少量的θ'相和S'相.二次时效促进强化相,特别是T1相的二次沉淀,提高合金的强度,同时几乎不损失塑性.     

气孔缺陷对TA15 钛合金氩弧焊接头疲劳性能的影响

对TA15钛合金氩弧焊接接头的组织和疲劳断裂特征进行了分析,对气孔缺陷和疲劳寿命的关系进行了定量表征.结果表明:疲劳裂纹起源于焊缝的亚表面或者内部气孔缺陷,当气孔尺寸较小时,断口会出现“鱼眼”形貌特征;应力水平较低时,气孔尺寸对疲劳寿命的影响尤为显著,在特定的应力水平下,可以通过构件中的气孔缺陷尺寸来预测其寿命,对于焊接结构疲劳寿命的预测和构件焊接质量的评定具有重要的工程意义.     

基于轮廓法测试铝合金拉弯成形残余应力研究

以2026-T3511铝合金T形结构件的拉弯成形件为研究对象,首先采用线切割将T形结构件分割成两块具有T形截面的试样,然后基于轮廓法测试应力原理应用激光位移传感器分别测试两个分割截面的轮廓变化,进而将两个截面的测量值拟合平均后与有限元模型结合以计算该试样的初始残余应力,从而获得该T形结构件的横截面法向应力并分析其分布特征。研究结果表明,基于轮廓法测得的应力分布与有限元仿真结果分布规律相近:峰值压应力为60MPa,峰值拉应力为40MPa;轮廓法在航空结构件应力测试中能够准确地获得其他测试方法无法获得的横截面完整的应力分布。     

高温长期时效对一种镍基单晶合金拉伸和持久性能的影响

研究了高温长期时效对一种镍基单晶合金在室温条件下瞬时拉伸强度和在950℃/240MPa条件下持久性能的影响。结果表明:1000℃短期时效100h,合金室温拉伸强度σb与屈服强度σ0.2与时效前相比没有明显变化,时效超过500h后σb和σ0.2开始显著下降,时效超过1000h后,σb和σ0.2随时效时间延长下降幅度减小;短期时效100h和500h样品在950℃/240MPa条件下的持久寿命大幅度降低,延伸率快速上升,时效时间超过1000h后,持久寿命的下降幅度减小,合金的持久寿命与延伸率均趋于稳定。长期时效后γ'相形貌改变及γ/γ'相界面高密度位错网的破坏是时效后合金室温及高温持久性能持续降低的主要原因。